63/37 Yellow Brass
63/37 Yellow Brass
Sunraj Industries exports 63/37 Brass which is also known as Common Brass and Yellow Brass. 63/37 Brasses are copper zinc alloys with a wide range of engineering uses. The addition of zinc to copper raises the strength and gives a range of properties, and the brasses are a very versatile range of materials.
They are used for their strength, corrosion resistance, appearance and colour, and ease of working and joining. The single phase alpha brasses, containing up to about 37% zinc, are very ductile and easy to cold work, weld and braze. The dual phase alpha-beta brasses are usually hot worked. Brasses are resistant to corrosion in many media.
63/37 Brass is widely used in Radiator Tanks and Cores, Flashlight Shells, Lamp Fixtures, Fastenerslocks, Hinges, Pins, Rivets, Buttons, Plumbing Accessories.
| Material | Normal Composition | Nearest Relevant Composition Specification | ||
| 63/37 Yellow Brass | 63% Cu, 37% Zn | CZ108 | Cu Zn 37 426/1 |
H 3100 C 3560 |
MECHANICAL PROPERTIES AS PER : B.S. : 2870 :
| Material | Temper | Tensile Strength N/mm2 | Elongation % on 50 mm G.L. | Vickers Hardness VPN | ISO | JIS |
| 63/37 Yellow Brass | AnnealedCondition('O') Quarter Hard (1/4H) Half Hard (1/2H) Hard (H) |
280 Min 340 Min 385 Min 460 Min |
40 Min 30 Min 15 Min 5 Min |
80 Max 75 Min 110 Min 135 Min |
Cu Zn 37 ISO:426/1 | JIS 3100 C 3560 |